Optimization of Oxygen Plasma based Etching of Single Layered Graphene through Raman and FESEM Characterization

Agarwal , PB and Paulchowdhury, P and Mukherjee, A and Lohani, P and Thakur, NK (2019) Optimization of Oxygen Plasma based Etching of Single Layered Graphene through Raman and FESEM Characterization. In: International Conference on Advances in Nanomaterials and Devices for Energy and Environment (ICAN-2019), January 27-29, 2019, ABV-IIITM, Gwalior.

[img]
Preview
PDF
Download (233Kb) | Preview

Abstract

Post-synthesis patterning of single layered graphene (SLG) is essential to realize graphene based novel devices and sensors in practical applications [1]. In this paper, oxygen plasma etching experiments over as grown SLG were carried out, which confirmed the complete etching of SLG layer in 240 s. SLG was grown over copper (Cu) foil by chemical vapor deposition (CVD) technique using methane (CH4) as precursor gas and hydrogen (H2) as carrier gas in a furnace heated to 1000 °C as shown in Fig. 1 (a). To transfer SLG on SiO2/Si substrate, PMMA was spin coated over the Cu-SLG film at 4000 rpm for 60 s, followed by etching of underlying Cu layer by dissolving it into FeCl3 solution. The SiO2/Si wafer was used to fish out the free flowing PMMA coated SLG from the FeCl3 solution, followed by thorough washing with DI water and ethanol. Acetone was used to remove the PMMA completely from the top; resulting in transferred SLG over SiO2 surface as shown in Fig. 1 (b). Etching experiments of SLG were carried out using oxygen plasma for 30 s, 90 s, 120 s, 150 s, and 240 s at 200 W RF (13.56 MHz) power, 0.8 torr pressure, and with 2-3 sccm oxygen flow. Raman spectra at different etching times confirm that the 2D peak almost disappear after 240 s of etching as depicted in Fig 1 (c). In addition, 1D/1G ratio increases from 0.17 (pristine) to 1.33 (150 s) with etching time, which indicates the breaking of the C-C bonds and finally leaving only amorphous carbon with residual C-C bond peaks in Raman spectra. FESEM in Fig. 1 (d), shows images of pristine graphene (before etch) and (e) is after 240 s of plasma etching, which shows complete etching.

Item Type: Conference or Workshop Item (Paper)
Subjects: Semiconductor Devices > Sensors and Nanotechnology
Divisions: Semiconductor Devices
Depositing User: Mr. Jitendra Nath Bajpai
Date Deposited: 29 Sep 2021 09:27
Last Modified: 29 Sep 2021 09:27
URI: http://ceeri.csircentral.net/id/eprint/606